| 245 |
1 |
0 |
|a Istraživanje fizičkih i mehaničkih svojstava fosfatnih uložnih materijala u ovisnosti o načinu pripreme :
|b doktorska disertacija /
|c Dragutin Komar.
|
| 260 |
|
|
|a Zagreb :
|b D. Komar,
|c 1997
|e ([s. l. :
|f s. n.])
|
| 300 |
|
|
|a 144 listova :
|b table, graf. prikazi ;
|c 30 cm.
|
| 500 |
|
|
|a Doktor medicinskih znanosti - stomatologija
|
| 500 |
|
|
|a Mentor: Biserka Lazić;
|
| 502 |
|
|
|a Sveučilište u Zagrebu, Stomatološki fakultet, Zagreb, 1997.
|
| 504 |
|
|
|a Bibliografija: str. 130-142
|
| 504 |
|
|
|a Summary
|
| 520 |
|
|
|a Sažetak: U radu je temeljem provedenih laboratorijskih istraživanja ispitan utjecaj varijacija sastava i načina pripreme fosfatnih uložnih materijala na njihove primjenske osobitosti. Za ispitivanje tlačne čvrstoće odnosno dimenzionalnih promjena fosfatnog uložnog materijala (vezivna i termička ekspanzija) učinjene su 42 međusobno različite skupine uložnog materijala načinjene od 6 istovremeno i istovjetno pripremljenih uzoraka. Tlačna čvrstoća uzoraka određena je prešom "Tonindustrie" u području sila od 0-20 kN. Hladna odnosno vezivna ekspanzija određena je uređajem za mjerenje autogenih deformacija žitkih građevinskih materijala koji je konstruiran na Institutu građevinarstva Hrvatske u Zagrebu. Termička ekspanzija fosfatnog uložnog materijala određena je ekspanzionim dilatometrom tipa "Chevenard".
|
| 520 |
|
|
|a Dobiveni rezultati istraživanja pokazuju da se tlačna čvrstoća smanjuje srazmjerno s porastom udjela ukupne tekućine u omjeru prah/tekućina, te da uz isti sadržaj ukupne tekućine veće čvrstoće pokazuju uzorci s višim koncentracijama ekspanzione tekućine. Osim toga, tlačne čvrstoće ručno pripremljenih uzoraka veće su u odnosu na vacuumski pripremljeni uložni materijal. Rasipanja rezultata kod mjerenja čvrstoća na pritisak na uzorcima istog sastava i načina pripreme manja su kod ručno pripremeljenih uzoraka (koeficijent varijacije 2,2 - 4,2%) u oodnosu na vacuumski pripremljene uzorke (K.v. 4,3- 5,9%). Vrijednosti vezivne ekspanzije ručno pripremljenih uzoraka (0,7%) više su za 0,4% u odnosu na vacuumski pripremljene uzorke (0,3%).
|
| 520 |
|
|
|a Termička ekspanzija obrnuto je razmjerna količini ukupne tekućine, a upravo je razmjerna količini ekspanzione komponente u ukupnoj količini tekućine. Osim toga, iskazane vrijednosti termičkih ekspanzija ručno pripremljenih uzorakauvijek su manje od uzoraka istog sastava pripremljenih vacuumskim miješanjem. Ukupna ekspanzija fosfatnog materijala za ulaganje veća je kod ručno pripremljenih uzoraka.
|
| 520 |
|
|
|a Summary: On the basis of laboratory research the influence of variations in content and method of preparation of phosphate investment materials on their application properties is discussed in the paper. In the examinations of compression strenght, i.e. dimensional changes in phosphate investment material (cohesive and thermic expansion), 42 different groups of investment materials were made containing 6 simuntaneously and identically prepared samples. Compresions strength was determined by "Tonindustrie" pressurizer in force range from 0 to 20 kN. Cold or cohesive expansion was determined by instrument employed in the measuremant of autogenous deformites of liquid materials used in construction industry and designed at State Institute of Civil Engineering in Zagreb.
|
| 520 |
|
|
|a Thermic expansion of phosphate investment materials was mesured by "Chevenard" type expansion dilatometer. The study results have shown that compresion strength diminishes proportionaly with the increase of total liquid volume in powder/liquid ratio, and that at an equal total liquid content the sample with greater concentrations of expansion liquid show greater compression strength. Besides, compression strength of manually prepared samples is greater than that of investment materials prepared by vacuum method. Dispersion of results has been observed to a lasser extent in the measurement of compression strength of samples of identical content and method of preparation in manually prepared samples (variation coefficient 2,2 - 4,2%) Than in those prepared by the vacuum method (variation coefficient 4,3 - 5,9%).
|
| 520 |
|
|
|a The values of cohesive expansion of manually prepared samples (0,7%) are for 0,4% higher in comparison with the samples prepared by the vacuum method (0,3%). Thermic expansion is inversely proportional to total liquid amount and directly proportional ot the amount of expansion component in the total liquid quantity.Furthermore, the values of thermic expansion in manually prepared samples are always smaller than those in the samples of the content but prepared by vacuum mixing method. The total expansion of phosphate investment material is greater in manually prepared samples.
|
| 650 |
|
7 |
|a Protetički materijali
|x Materijali za ulaganje
|2 nskps
|
| 700 |
1 |
|
|a Lazić, Biserka
|4 cns
|
| 981 |
|
|
|p CRO
|r HRB1997
|
| 998 |
|
|
|n DCD/97
|c dkro9911
|
| 852 |
4 |
|
|j DCD-ZG-200/98
|
| 876 |
|
|
|e DCD
|a 200/1998
|
| 886 |
0 |
|
|2 unimarc
|b 05233nam0 2200349 450
|