Some characteristic physical properties of nickel oxide powder
Nickel oxide powder was prepared by firing spec pure NiCO3 in air for 6 hours at different firing temperatures ranged from 800°C to 1200 °C. The crystal structure of all samples is a cubic structural as obtained from XRD study. The diffuse reflectance of different samples of NiO was measured at room...
| Permalink: | http://skupni.nsk.hr/Record/nsk.NSK01000744715/Details |
|---|---|
| Matična publikacija: |
Fizika A (Zagreb) 18 (2009), 1/4 ; str. 173-184 |
| Glavni autor: | Gad, S. A. (-) |
| Ostali autori: | Boshta, M. (-), El-Soud, Aziza A. Abo, Mostafa, M. Z. |
| Vrsta građe: | Članak |
| Jezik: | eng |
| Predmet: | |
| Online pristup: |
http://fizika.hfd.hr/fizikaa.htm |
| LEADER | 02221caa a2200325 i 4500 | ||
|---|---|---|---|
| 001 | NSK01000744715 | ||
| 003 | HR-ZaNSK | ||
| 005 | 20210309164532.0 | ||
| 007 | ta | ||
| 008 | 100930s2009 ci ||| ||eng | ||
| 035 | |a (HR-ZaNSK)000744715 | ||
| 040 | |a HR-ZaNSK |b hrv |c HR-ZaNSK |e ppiak | ||
| 041 | 0 | |a eng |b hrv | |
| 042 | |a croatica | ||
| 044 | |a ci |c hr | ||
| 080 | |a 53 |2 MRF 1998. | ||
| 100 | 1 | |a Gad, S. A. | |
| 245 | 1 | 0 | |a Some characteristic physical properties of nickel oxide powder / |c S. A. Gad, M. Boshita, A. M. Abo El-Soud and M. Z. Mostafa. |
| 300 | |b Ilustr. | ||
| 504 | |a Bibliografija: 22 jed. | ||
| 504 | |a Sažetak | ||
| 520 | |a Nickel oxide powder was prepared by firing spec pure NiCO3 in air for 6 hours at different firing temperatures ranged from 800°C to 1200 °C. The crystal structure of all samples is a cubic structural as obtained from XRD study. The diffuse reflectance of different samples of NiO was measured at room temperature in the wavelength range from 200 to 2000 nm. The energy gap of NiO samples was then deduced as well as the position and number of different transitions which were found to be dependent on the firing temperature. The electrical conductivity sm was measured over temperature range from 50°C to 320 °C and frequency range from 42 Hz to 5 MHz. The conductivity decreases with increasing firing temperature and increases with frequency. The activation energy was calculated and was found to increase with increasing firing temperature. Electron spin resonance (ESR) spectra were recorded at room temperature as first derivatives using an X-band spectrometer with a magnetic field modulation of 100 kHz. The intensity of the ESR-spectra of NiO samples decreases with increasing firing temperature | ||
| 653 | 0 | |a Nikal oksid |a Prah |a Fizikalna svojstva |a Kristalna struktura |a Elektronska spinska rezonancija |a Električna vodljivost |a Aktivacijska energija |a Sobna temperatura |a Visoke temperature | |
| 700 | 1 | |a Boshta, M. | |
| 700 | 1 | |a El-Soud, Aziza A. Abo | |
| 700 | 1 | |a Mostafa, M. Z. | |
| 773 | 0 | |t Fizika A (Zagreb) |x 1330-0008 |g 18 (2009), 1/4 ; str. 173-184 | |
| 981 | |b B09/09 |p CRO | ||
| 998 | |a rado100930 |c vol2o121005 | ||
| 856 | 4 | 2 | |u http://fizika.hfd.hr/fizikaa.htm |